This product series is a thermosetting powder coating made by melt-extruding and grinding saturated polyester resin with excellent weather resistance, combined with TGIC curing agent, along with necessary pigments, fillers, and additives. It boasts outstanding physical, chemical, and decorative properties. Depending on requirements, this product series can be formulated into products with varying curing temperatures (140℃ to 200℃), different textures (smooth, sand-textured, or brushed), and different gloss levels (from 20% to 95%).

Keywords:

Davao Powder

Category:

IT equipment powder coating

Product Inquiry
Featured product

Share to

Facebook Linkedin Twitter Tumblr Pinterest
  • Product Details

  • Product Description

    This product series is a thermosetting powder coating made by melt-extruding and grinding saturated polyester resin with excellent weather resistance, combined with TGIC curing agent, along with necessary pigments, fillers, and additives. It boasts outstanding physical, chemical, and decorative properties. Depending on requirements, this product series can be formulated into products with varying curing temperatures (140℃ to 200℃), different textures (smooth, sand-textured, or droplet-like), and different gloss levels (from 20% to 95%).

     

    Storage conditions

    Under conditions where the temperature is below 30℃ and the relative humidity is below 60%, the shelf life is 6 months. If the shelf life exceeds 6 months, the product must undergo re-inspection before it can be used.

     

    Powder curing requirements

    180℃ for 15 minutes (workpiece temperature); 200℃ for 10 minutes (workpiece temperature); for matte finishes, extend the time by 5 minutes—refer to the product’s test report for details.

    For standard products, the coating thickness typically ranges from 60 to 80 μm; for textured products, the coating thickness varies depending on the size of the texture. Exceeding the specified coating thickness may result in pinholes or inconsistencies in texture appearance. The relevant test results are obtained under the premise of substrate materials and operational processes and parameters that meet the corresponding standard requirements (or specific specifications). These results may differ from the actual effects achieved using the customer’s own operational processes and parameters on their substrates. Furthermore, the tests were conducted under laboratory conditions and are provided for reference only.

     

    Operation Process and Parameters

    • Common steel, zinc phosphate treatment
    • Galvanized steel sheet, iron phosphate treatment
    • Aluminum material, chromate treatment

    Before the above processing steps, the substrate must be thoroughly cleaned to remove any oil and grease, and then dried. The drying temperature should not exceed 200℃ to avoid damaging the operational process and film parameters, which could result in the final powder coating performance failing to meet the required standards.

    Before spraying castings (especially those that have been poured) and hot-dip galvanized parts, it is essential to heat them at high temperature to remove any internal moisture and gases, thus preventing bubble formation. Please also notify us in advance so that we can make appropriate adjustments to the formulation.

    Note: Customers should periodically inspect the quality of operating procedures and parameters according to their supplier’s requirements.